On the magnetic properties of mechanosynthesized Co-Fe-Ni ternary alloys
Artykuł w czasopiśmie
MNiSW
25
Lista A
| Status: | |
| Autorzy: | Jartych Elżbieta |
| Rok wydania: | 2011 |
| Wersja dokumentu: | Elektroniczna |
| Język: | angielski |
| Numer czasopisma: | 2 |
| Wolumen/Tom: | 323 |
| Strony: | 209 - 216 |
| Impact Factor: | 1,78 |
| Web of Science® Times Cited: | 35 |
| Scopus® Cytowania: | 35 |
| Bazy: | Web of Science | Scopus |
| Efekt badań statutowych | NIE |
| Materiał konferencyjny: | NIE |
| Publikacja OA: | NIE |
| Abstrakty: | polski |
| X-ray diffraction, Mossbauer spectroscopy and magnetization measurements were used as complementary methods to obtain structural data and to determine magnetic properties of the mechanically synthesized and subsequently thermally treated Co-Fe-Ni alloys. New, however approximate, phase diagrams were established on the basis of X-ray diffraction investigations. Mossbauer spectroscopy and magnetization measurements allowed to reveal practically linear correlation between the average values of the hyperfine magnetic field induction, < B-hf >, and the effective magnetic moments, mu(eff), of the alloys. The decrease in < B-hf > with the number of electrons per atom, e/a, was observed. Moreover, the dependence of mu(eff) on the valence 3d and 4s electrons per atom follows the Slater-Pauling curve. Thermal treatment of mechanosynthesized Co-Fe-Ni alloys led to some changes in the phase diagrams, increase in the grain size and decrease of the level of internal strains in alloys. Dependencies of lattice constants, average hyperfine magnetic fields, effective magnetic moments and Curie temperatures on the number of electrons per atom have the same trends for mechanically synthesized as well as for thermally treated alloys. |