Profile and Areal Surface Parameters for Fatigue Fracture Characterisation
Artykuł w czasopiśmie
MNiSW
140
Lista 2021
| Status: | |
| Autorzy: | Macek Wojciech, Branco Ricardo, Szala Mirosław, Marciniak Zbigniew, Ulewicz Robert, Szczygioł Norbert, Kardasz Piotr |
| Dyscypliny: | |
| Aby zobaczyć szczegóły należy się zalogować. | |
| Rok wydania: | 2020 |
| Wersja dokumentu: | Drukowana | Elektroniczna |
| Język: | angielski |
| Numer czasopisma: | 17 |
| Wolumen/Tom: | 13 |
| Numer artykułu: | 3691 |
| Strony: | 1 - 14 |
| Impact Factor: | 3,623 |
| Web of Science® Times Cited: | 40 |
| Scopus® Cytowania: | 42 |
| Bazy: | Web of Science | Scopus |
| Efekt badań statutowych | NIE |
| Finansowanie: | The project/research was financed in the framework of the project Lublin University of Technology—Regional Excellence Initiative, funded by the Polish Ministry of Science and Higher Education (contract no. 030/RID/2018/19). |
| Materiał konferencyjny: | NIE |
| Publikacja OA: | TAK |
| Licencja: | |
| Sposób udostępnienia: | Witryna wydawcy |
| Wersja tekstu: | Ostateczna wersja opublikowana |
| Czas opublikowania: | W momencie opublikowania |
| Data opublikowania w OA: | 20 sierpnia 2020 |
| Abstrakty: | angielski |
| Post-mortem characterisation is a pivotal tool to trace back to the origin of structural failures in modern engineering analyses. This work compared both the crack propagation and rupture roughness profiles based on areal parameters for total fracture area. Notched and smooth samples made of weather-resistant structural steel (10HNAP), popular S355J2 structural steel and aluminium alloy AW-2017A under bending, torsion and combined bending–torsion were investigated. After the fatigue tests, fatigue fractures were measured with an optical profilometer, and the relevant surface parameters were critically compared. The results showed a great impact of the loading scenario on both the local profiles and total fracture areas. Both approaches (local and total fracture zones) for specimens with different geometries were investigated. For all specimens, measured texture parameters decreased in the following order: total area, rupture area and propagation area. |