The Effect of the Aging Process on Selected Properties of Polypropylene Modified by Natural Fillers
Artykuł w czasopiśmie
MNiSW
100
Lista 2021
| Status: | |
| Autorzy: | Samujło Bronisław |
| Dyscypliny: | |
| Aby zobaczyć szczegóły należy się zalogować. | |
| Rok wydania: | 2020 |
| Wersja dokumentu: | Drukowana | Elektroniczna |
| Język: | angielski |
| Numer czasopisma: | 4 |
| Wolumen/Tom: | 14 |
| Strony: | 139 - 147 |
| Web of Science® Times Cited: | 4 |
| Scopus® Cytowania: | 4 |
| Bazy: | Web of Science | Scopus | BazTech | Index Copernicus | Google Scholar |
| Efekt badań statutowych | NIE |
| Materiał konferencyjny: | NIE |
| Publikacja OA: | TAK |
| Licencja: | |
| Sposób udostępnienia: | Otwarte czasopismo |
| Wersja tekstu: | Ostateczna wersja opublikowana |
| Czas opublikowania: | W momencie opublikowania |
| Data opublikowania w OA: | 1 grudnia 2020 |
| Abstrakty: | angielski |
| The purpose of the research was to determine the aging-induced changes in the selected mechanical properties and flammability of polypropylene modified with natural fillers (sunflower husk, wheat bran, pine sawdust and talc). The fillers were introduced into polypropylene in a mechanical mixing process (weight content 20%). The samples were obtained with the use of an Allrounder 320 C500–170 laboratory injection molding machine. The ag-ing process under artificial sample conditions was carried out in the laboratory chamber (aging time of 0, 60, 120, 240, 360 hours). The tests of the mechanical properties included the measurements of hardness, impact strength and tensile strength. The flammability tests were carried out with a vertical and horizontal alignment of the sample according to the PN-EN 60695–11–10 standard. As a result of the research, a significant impact of the introduction of natural fillers in the form of sunflower husks, wheat bran and pine sawdust on the selected properties of polypro-pylene was demonstrated. A large decrease in the impact toughness, a relatively small decrease in the short-term tensile strength as well as an increase in the elastic modulus and stress at rupture caused by the introduction of the natural fillers mentioned, were found. A beneficial effect was the relatively small impact of aging on the mechani-cal properties and flammability of the modified polypropylene fillers. |