Processing aspects of p-v-T relationship
Artykuł w czasopiśmie
| Status: | |
| Warianty tytułu: |
Przetwórcze wykorzystanie zależności p-v-T
|
| Autorzy: | Kowalska Beata |
| Rok wydania: | 2006 |
| Wersja dokumentu: | Drukowana | Elektroniczna |
| Język: | angielski |
| Numer czasopisma: | 11-12 |
| Wolumen/Tom: | 51 |
| Strony: | 862 - 865 |
| Impact Factor: | 1,137 |
| Bazy: | BazTech |
| Efekt badań statutowych | NIE |
| Materiał konferencyjny: | NIE |
| Publikacja OA: | NIE |
| Abstrakty: | angielski | polski |
| The pressure-specific volume-temperature (p-v-T) relationship of polymers are important for the analysis of injection molding process. In the study, the p-v-T data for polypropylene Malen P type J-400 were measured during slow isobaric cooling. From the results of these measurements, the p-v-T data of the amorphous and semi-crystalline phases were obtained. The crystallization kinetics of the sample was determined using DSC measurements and the results have been fitted to the Nakamura-Hieber model to obtain equation parameters. Then the p-v-T behavior corresponding to the high cooling rate used in molding process was obtained. | |
| Znajomość zależności ciśnienie-objętość właściwa-temperatura (p-v-T) dotyczących polimerów jest istotna w analizie procesu wtryskiwania. W ramach tej pracy wyznaczono zmiany v podczas powolnego izobarycznego ochładzania polipropylenu (Malen P typ J-400) stosując różne wartości ciśnienia z przedziału 0,1-160 MPa (rys. 1). Otrzymane wyniki opisano za pomocą równania Taita określając parametry dobierane odnoszące się do stanu ciekłego i stałego polimeru (tabela 1 i 2). Kinetykę krystalizacji próbek wyznaczano za pomocą pomiarów DSC (rys. 2), a wyniki opisano korzystając z modelu Nakamury-Hiebera (tabela 3). Za pomocą symulacji komputerowej określono zależność p-v-T odpowiadającą wysokim szybkościom chłodzenia polimeru, czyli takim jakie stosuje się w procesie wtryskiwania. |