Adhesion is a surface phenomenon occurring in many processes, e.g., bonding, painting or varnishing. Knowing the adhesion properties is critical for evaluating the usability or behaviour of materials during these processes. Good adhesion properties favour the processes of bonding, resulting in high strength of adhesive joints. Adhesive bonded joints are used in many industries, and the subject of this study was 7075 aluminium alloy sheet bonded joints as typically used in the aviation or construction industry. Surface free energy (SFE) can be used to determine the adhesion properties of the materials. The SFE of the tested sheets was determined with the Owens–Wendt method, which consists in determining the dispersion and polar components of SFE. The purpose of this work was to correlate the bonded joint strength of selected aluminium alloy sheets to the surface free energy of the sheets that had been subjected to degreasing only and no other prior treatment was used. Single-lap bonded joints of 7075 aluminium alloy sheets were tested. Higher joint strength was measured for the thinner sheets, while the lowest strength was measured for the thickest sheets. This suggests that the thickness of the joined parts is an important factor in the strength of bonded joints. The comparison of adhesion properties to the strength of adhesive joints of tested materials shows that there is no direct relation between good adhesion properties (i.e., high SFE) and joint strength. As for degreasing, the highest joint strength was observed for aluminium alloy sheets with the lowest SFE; the sheets which were not degreased gave the highest SFE and highest joint strength.
|