Mechanical Properties of Selected Epoxy Adhesive and Adhesive Joints of Steel Sheets
Artykuł w czasopiśmie
MNiSW
5
spoza listy
| Status: | |
| Autorzy: | Rudawska Anna |
| Dyscypliny: | |
| Aby zobaczyć szczegóły należy się zalogować. | |
| Rok wydania: | 2021 |
| Wersja dokumentu: | Drukowana | Elektroniczna |
| Język: | angielski |
| Numer czasopisma: | 1 |
| Wolumen/Tom: | 2 |
| Strony: | 108 - 126 |
| Web of Science® Times Cited: | 15 |
| Scopus® Cytowania: | 17 |
| Bazy: | Web of Science | Scopus |
| Efekt badań statutowych | NIE |
| Materiał konferencyjny: | NIE |
| Publikacja OA: | TAK |
| Licencja: | |
| Sposób udostępnienia: | Witryna wydawcy |
| Wersja tekstu: | Ostateczna wersja opublikowana |
| Czas opublikowania: | W momencie opublikowania |
| Data opublikowania w OA: | 3 marca 2021 |
| Abstrakty: | angielski |
| The article presents the issues of the mechanical properties of epoxy adhesives and the adhesive joints strength of steel sheets which were made using the epoxy adhesives. The aim of the paper is to study the mechanical properties of epoxy adhesive of different epoxy resin/curing agent ratios (within and above the recommended stoichiometric ratio) and their effect on mechanical properties of adhesive joints of steel sheets. In experimental tests three types of epoxy adhesives, containing a low molecular weight epoxy resin based on bisphenol A and polyamide curing agent, were used. A single-lap adhesive joint type of stainless-steel sheets was also applied. Two types of strength test were used: the compressive strength tests (DIN EN 196-1) for epoxy adhesive samples and the shear strength tests (DIN EN 1465) for adhesive joints. Both the analysis of the strength results of the samples of epoxy adhesive and adhesive joints as well as the failure analysis was carried out. On the basis of the results of strength tests it can be stated that the greatest deformation occurred for the samples of epoxy adhesive containing the modified epoxy resin (epoxy number—0.40) and the polyamide curing agent, and the smallest for the samples of epoxy adhesive containing the basic epoxy resin (epoxy number—0.49–0.52) and the polyamide curing agent. The epoxy adhesives with a smaller amount of curing agent were characterized by higher strength. This applies to all analyzed epoxy resins. The same dependences were obtained for the strength of adhesive joints of steel sheets made of the analyzed epoxy adhesive. |