Baza Publikacji Pracowników Politechniki Lubelskiej

Status:
Autorzy:	Rudawska Anna, Miturska-Barańska Izabela, Doluk Elżbieta
Dyscypliny:
	Aby zobaczyć szczegóły należy się zalogować.
Rok wydania:	2021
Wersja dokumentu:	Drukowana \| Elektroniczna
Język:	angielski
Numer czasopisma:	22
Wolumen/Tom:	14
Numer artykułu:	6938
Strony:	1 - 23
Impact Factor:	3,748
Web of Science® Times Cited:	10
Scopus® Cytowania:	11
Bazy:	Web of Science \| Scopus
Efekt badań statutowych	NIE
Finansowanie:	The project/research was financed in the framework of the project Lublin University of Technology—Regional Excellence Initiative, funded by the Polish Ministry of Science and Higher Education (contract no. 030/RID/2018/19).
Materiał konferencyjny:	NIE
Publikacja OA:	TAK
Licencja:
Sposób udostępnienia:	Witryna wydawcy
Wersja tekstu:	Ostateczna wersja opublikowana
Czas opublikowania:	W momencie opublikowania
Data opublikowania w OA:	16 listopada 2021
Abstrakty:	angielski
	The purpose of the paper is to determine the impact of surface treatment on the strength of adhesive joints, made from various steel sheets. Two variants of the surface treatment steel adherends were used: without the varnish coat and with the varnish coat, using three polymer-based varnishes (a simple, a hybrid, and a gel). Two types of the adhesives were used to prepare the adhesive joints: a single-component cyanoacrylate adhesive and a two-component epoxy adhesive. A strength test of the adhesive joints (EN DIN 1465 standard), a coating adhesion test (ASTM D3359-B standard), and surface topography, as well as surface roughness, parameters (PN-EN ISO 11562, PN-EN ISO 4287, and PN-EN ISO 25178 standards) were used. Based on the strength tests, it was observed that the adhesive joints, with the hybrid varnish onto the adherend’s surface, achieved markedly lower shear strength. The best results, in terms of the adhesive joint strength, made using the cyanoacrylate adhesive were achieved for the joints where the adherends were coated with a simple varnish, while in the joints made using the epoxy adhesive, the highest shear strength was achieved by the joints of sheets whose surfaces were coated with the gel varnish.

Informacja o cookies

Influence of Surface Treatment on Steel Adhesive Joints Strength—Varnish Coats