The Influence of Gum Arabic Admixture on the Mechanical Properties of Lime-Metakaolin Paste Used as Binder in Hemp Concrete
Artykuł w czasopiśmie
MNiSW
140
Lista 2021
| Status: | |
| Autorzy: | Brzyski Przemysław |
| Dyscypliny: | |
| Aby zobaczyć szczegóły należy się zalogować. | |
| Rok wydania: | 2021 |
| Wersja dokumentu: | Drukowana | Elektroniczna |
| Język: | angielski |
| Numer czasopisma: | 22 |
| Wolumen/Tom: | 14 |
| Numer artykułu: | 6775 |
| Strony: | 1 - 22 |
| Web of Science® Times Cited: | 6 |
| Scopus® Cytowania: | 13 |
| Bazy: | Web of Science | Scopus |
| Efekt badań statutowych | NIE |
| Finansowanie: | This research was funded by the Narodowe Centrum Nauki in Poland (National Science Center, Poland) under grant number 2019/03/X/ST8/01950. |
| Materiał konferencyjny: | NIE |
| Publikacja OA: | TAK |
| Licencja: | |
| Sposób udostępnienia: | Witryna wydawcy |
| Wersja tekstu: | Ostateczna wersja opublikowana |
| Czas opublikowania: | W momencie opublikowania |
| Data opublikowania w OA: | 10 listopada 2021 |
| Abstrakty: | angielski |
| Organic admixtures based on polysaccharides are used in construction for modifying the properties of mortars and concretes. Gum arabic is an example of a polysaccharide-based biopolymer. The aim of the article was to investigate the possibilities of improving the strength parameters of a binder paste based on hydrated lime and metakaolin. The paste was modified with powdered gum arabic at 1%, 3% and 5% (by mass) as a partial replacement for the binder mix. The influence of the admixture on the pore size distribution as well as flexural and compressive strength was investigated. The admixture enhanced the total porosity of the paste, increasing the pore diameter compared with the reference formulation. The increase in porosity, in turn, did not reduce the mechanical strength. Conversely, the admixture in the amount of 3% and 5% caused a significant increase in the flexural (by about 300% in relation to reference paste) and compressive strengths (by 25% and 60%, respectively). The tested pastes were used as a binder in a composite based on hemp shives. The influence of binder modification on the water absorption and compressive strength of hemp concrete was tested. The strength of the composite soaked in water was also tested. The modification of the binder with gum arabic in the amount of 3% and 5% increased the compressive strength of hemp concrete (not soaked in water) by 53% and 92%, respectively and reduced the mass absorptivity by 6.6% and 10.4%, respectively. |