Influence of Adhesive Compound Viscosity on the Strength Properties of 1.0503 Steel Sheets Adhesive Joints
Artykuł w czasopiśmie
MNiSW
100
Lista 2021
| Status: | |
| Autorzy: | Miturska-Barańska Izabela, Rudawska Anna |
| Dyscypliny: | |
| Aby zobaczyć szczegóły należy się zalogować. | |
| Rok wydania: | 2022 |
| Wersja dokumentu: | Drukowana | Elektroniczna |
| Język: | angielski |
| Numer czasopisma: | 2 |
| Wolumen/Tom: | 16 |
| Strony: | 196 - 205 |
| Impact Factor: | 1,1 |
| Web of Science® Times Cited: | 2 |
| Scopus® Cytowania: | 2 |
| Bazy: | Web of Science | Scopus | Baztech |
| Efekt badań statutowych | NIE |
| Finansowanie: | This work was financed from the funds of the Ministry of Education and Science by Agreement No. DNK/ SP/513880/2021 of 22 December 2021, the project “14th School of Machining and the 43rd Scientific School of Abrasive Machining”, under the programme “Perfect Science”. |
| Materiał konferencyjny: | NIE |
| Publikacja OA: | TAK |
| Licencja: | |
| Sposób udostępnienia: | Otwarte czasopismo |
| Wersja tekstu: | Ostateczna wersja opublikowana |
| Czas opublikowania: | W momencie opublikowania |
| Data opublikowania w OA: | 22 marca 2022 |
| Abstrakty: | angielski |
| The presented study concerned the comparison of the adhesive joints strengths of 1.0503 carbon steel sheets of higher quality, which were made using adhesive compounds characterized by different viscosity index of the com- ponents. Three types of commercial epoxy resins were used: Epidian 5, Epidian 53 and Epidian 57, as well as two types of curing agents: polyamide (PAC) and amine (Z-1). The surfaces of the test specimens were subjected to a pre-treatment operation in the process of a mechanical machining with an abrasive coated tool of P320 grada- tion. The surface roughness measurements were carried out as a control. The single-lap adhesive joints were the subject of the strength testing. The strength tests carried out on a Zwick/Roell Z150 testing machine concerned the comparison of the strength of the adhesive joints loaded in shear. Statistical analysis was performed on the results obtained. It was observed, among others, that the adhesive joints prepared with the epoxy adhesive compounds containing the polyamide curing agent showed much higher the shear strength than the adhesive joints made with the epoxy adhesive compounds containing the amine curing agent. Moreover, the use of the polyamide curing agent in the adhesive compounds with the epoxy resins resulted in formation of a more elastic adhesive layer, for which higher elongation was observed than in the case of the epoxy compound with the amine curing agent. |