Temperature Effect on Buckling Properties of Thin-Walled Composite Profile Subjected to Axial Compression
Artykuł w czasopiśmie
MNiSW
100
Lista 2024
| Status: | |
| Autorzy: | Falkowicz Katarzyna, Kuciej Michał, Święch Łukasz |
| Dyscypliny: | |
| Aby zobaczyć szczegóły należy się zalogować. | |
| Rok wydania: | 2024 |
| Wersja dokumentu: | Drukowana | Elektroniczna |
| Język: | angielski |
| Numer czasopisma: | 3 |
| Wolumen/Tom: | 18 |
| Strony: | 305 - 313 |
| Scopus® Cytowania: | 0 |
| Bazy: | Scopus | BazTech |
| Efekt badań statutowych | NIE |
| Finansowanie: | The research leading to these results has received funding from the commissioned task entitled “VIA CARPATIA Universities of Technology Network named after the President of the Republic of Poland Lech Kaczyński” contract no. MEiN/2022/DPI/2575 action entitled “In the neighborhood – inter-university research internships and study visits.” |
| Materiał konferencyjny: | NIE |
| Publikacja OA: | TAK |
| Licencja: | |
| Sposób udostępnienia: | Otwarte czasopismo |
| Wersja tekstu: | Ostateczna wersja opublikowana |
| Czas opublikowania: | W momencie opublikowania |
| Data opublikowania w OA: | 20 kwietnia 2024 |
| Abstrakty: | angielski |
| This study investigates the influence of temperature variations on the buckling properties of thin-walled omega-pro- files fabricated from carbon-epoxy composite materials. Utilizing a MTS testing machine, compression tests were conducted on these profiles at temperatures ranging from -20°C to 80°C, in 20°C increments. The primary objective was to assess how temperature fluctuations impact the buckling load and load-bearing capacity of these composite profiles under axial compression. The experimental setup allowed for precise measurement of load-displacement and load-deflection characteristics, and the critical load at which buckling initiation occurred. Observations revealed that the buckling resistance of the profiles exhibited a complex dependence on temperature. At lower temperatures, the composite material demonstrated enhanced stiffness and strength, marginally increasing buckling resistance. Conversely, at elevated temperatures, a noticeable degradation in mechanical properties was observed, leading to a reduced buckling load and altered failure modes. To complement the experimental findings, a comprehensive finite element (FE) analysis was conducted for sample in room temperature. The FE model, developed to replicate the experimental conditions closely, employed an eigenvalue-based approach to predict the buckling initiation and progression accurately. The presented results are the results of only preliminary tests and they will be expand about more samples number as well as to determine material properties for various temperatures. |