The Effect of Self-Healing Microcapsules in Corrosion Testing on Magnesium AZ31 Alloy and Fibre Metal Laminates
Artykuł w czasopiśmie
MNiSW
100
Lista 2024
Status: | |
Autorzy: | Ostapiuk Monika, Bieniaś Jarosław, Loureiro Mónica V., Marques Ana C. |
Dyscypliny: | |
Aby zobaczyć szczegóły należy się zalogować. | |
Rok wydania: | 2024 |
Wersja dokumentu: | Drukowana | Elektroniczna |
Język: | angielski |
Numer czasopisma: | 6 |
Wolumen/Tom: | 14 |
Numer artykułu: | 653 |
Strony: | 1 - 14 |
Impact Factor: | 2,9 |
Web of Science® Times Cited: | 0 |
Scopus® Cytowania: | 0 |
Bazy: | Web of Science | Scopus |
Efekt badań statutowych | NIE |
Finansowanie: | The research was conducted thanks to funding from the Polish National Agency for Academic Exchange, known as the Bekker program [No. PPN/BEK/2018/1/00213]. The authors gratefully acknowledge Fundacão para a Ciência e a Tecnologia (FCT) through the support of CERENA (Strategic Project FCT-UIDB/04028/2020). The work was developed under COST Action CA18120—“CERTBOND-Reliable roadmap for certification of bonded primary structures”. |
Materiał konferencyjny: | NIE |
Publikacja OA: | TAK |
Licencja: | |
Sposób udostępnienia: | Witryna wydawcy |
Wersja tekstu: | Ostateczna wersja opublikowana |
Czas opublikowania: | W momencie opublikowania |
Data opublikowania w OA: | 21 maja 2024 |
Abstrakty: | angielski |
Fibre metal laminates (FMLs) are the most interesting composite materials of the past decade. They possess the properties of both polymer composites and metallic alloys. However, there is a problem with corrosion when the outer layers are made of aluminium or magnesium. The electrochemical changes that occur during the corrosion process and the mechanisms associated with the corrosion phenomenon are still being investigated. Recently, self-healing phenomena have emerged as a useful approach to prevent corrosion. However, there is limited research on the combination of FMLs and self-healing layers. Therefore, the main purpose of this article is to evaluate the self-healing ability of a magnesium/PEO layer based on microcapsules in a corrosion environment. It was observed that the corrosion mechanism in magnesium alloys is very complex. However, the use of a barrier layer with PEO treatment and microcapsules yielded positive anti-corrosion results. The FML samples were subjected to a 6-week corrosion test, and the addition of microcapsules to the layers showed positive results. In contrast, the samples without microcapsules exhibited intergranular corrosion. In the future, comprehensive tests using self-healing microcapsules in FMLs could greatly enhance their anti-corrosion properties and improve the integrity of the structure. |