Evaluation of the Effectiveness of Surface Defect Removal by Slide Burnishing
Artykuł w czasopiśmie
MNiSW
100
Lista 2024
| Status: | |
| Autorzy: | Skoczylas Agnieszka, Zaleski Kazimierz, Matuszak Jakub |
| Dyscypliny: | |
| Aby zobaczyć szczegóły należy się zalogować. | |
| Rok wydania: | 2025 |
| Wersja dokumentu: | Drukowana | Elektroniczna |
| Język: | angielski |
| Numer czasopisma: | 13 |
| Wolumen/Tom: | 15 |
| Strony: | 1 - 18 |
| Impact Factor: | 2,5 |
| Web of Science® Times Cited: | 0 |
| Scopus® Cytowania: | 0 |
| Bazy: | Web of Science | Scopus |
| Efekt badań statutowych | NIE |
| Materiał konferencyjny: | NIE |
| Publikacja OA: | TAK |
| Licencja: | |
| Sposób udostępnienia: | Witryna wydawcy |
| Wersja tekstu: | Ostateczna wersja opublikowana |
| Czas opublikowania: | W momencie opublikowania |
| Data opublikowania w OA: | 1 lipca 2025 |
| Abstrakty: | angielski |
| This study determines the influence of technological parameters of slide burnishing on the size of surface defects (scratches). The experiment was performed on ring-shaped samples of C45 steel. The samples had scratches made on their surface with a nominal depth from 10 μm to 70 μm. Slide burnishing was carried out using a variable force and feed. It was observed that regardless of the applied force and feed, scratches with a nominal depth of 10 μm and 20 μm were completely removed, and a “crushing” effect occurred. As for other surface defects, they were 2 to 27 times smaller compared to their values before burnishing. The surface roughness parameters Ra, Rt, Rpk, Rk, and Rvk decreased. Their values were 42% to 91% lower than those observed after grinding. The thickness of the strengthened layer ranged from 10 μm to 15 μm, and the degree of strengthening was from 20% to 38% at a depth of 1 μm. Compressive residual stresses occurred in the surface layer. Taking into account the surface layer properties and the effectiveness of surface defect removal, it should be noted that the most beneficial effects were obtained at F = 150 N and f = 0.03 mm/rev. |