Fatigue Damage Mechanisms and Complementary Non-Destructive Testing of Thin-Walled Structures with Various Composite Material Lay-Ups
Artykuł w czasopiśmie
MNiSW
140
Lista 2024
| Status: | |
| Autorzy: | Różyło Patryk, Paśnik Jakub, Stawiarski Adam, Chwał Małgorzata, Romanowicz Paweł J., Barski Marek |
| Dyscypliny: | |
| Aby zobaczyć szczegóły należy się zalogować. | |
| Rok wydania: | 2026 |
| Wersja dokumentu: | Drukowana | Elektroniczna |
| Język: | angielski |
| Numer czasopisma: | 21 |
| Wolumen/Tom: | 19 |
| Numer artykułu: | 4726 |
| Strony: | 1 - 32 |
| Impact Factor: | 3,7 |
| Web of Science® Times Cited: | 0 |
| Bazy: | Web of Science |
| Efekt badań statutowych | NIE |
| Materiał konferencyjny: | NIE |
| Publikacja OA: | TAK |
| Licencja: | |
| Sposób udostępnienia: | Witryna wydawcy |
| Wersja tekstu: | Ostateczna wersja opublikowana |
| Czas opublikowania: | W momencie opublikowania |
| Data opublikowania w OA: | 6 listopada 2026 |
| Abstrakty: | angielski |
| This paper focuses on the fatigue response of composite structures, considering comple- mentary (different) non-destructive testing (NDT) techniques. The research concerns thin-walled profiles with a notch and several different composite material layer arrangements (composite lay-ups). The research determined the influence of the layer arrangement on fatigue strength and laminate damage forms. A fatigue testing device, passive thermography to assess thermal changes, acoustic emission to detect damage initiation and digital microscopy to analyse damage forms were utilised in the research. The correct parameters for fatigue testing were determined during the test trials to ensure that the test specimens did not lose their load-carrying capacity. The research aimed to analyse the phenomenon of composite failure during fatigue testing in quantitative and qualitative aspects. The study only considered fatigue response in the context of permissible operating loads—excluding tests that took into account the total failure of the specimens. |