Mechanical Properties and Microstructure of Bonded Joints and Hybrid Structures with a 3D-Printed Honeycomb Core Modified with an Epoxy Matrix Filled with Recycled Polyurethane Foam
Artykuł w czasopiśmie
MNiSW
140
Lista 2024
| Status: | |
| Autorzy: | Penc Michal, Müller Miroslav, Marčan Jiří, Mishra Rajesh Kumar, Svobodova Jaroslava, Jirků Petr, Rudawska Anna, Valášek Petr |
| Dyscypliny: | |
| Aby zobaczyć szczegóły należy się zalogować. | |
| Rok wydania: | 2026 |
| Wersja dokumentu: | Drukowana | Elektroniczna |
| Język: | angielski |
| Numer czasopisma: | 18 |
| Wolumen/Tom: | 19 |
| Numer artykułu: | 3935 |
| Strony: | 1 - 27 |
| Impact Factor: | 3,7 |
| Web of Science® Times Cited: | 0 |
| Scopus® Cytowania: | 0 |
| Bazy: | Web of Science | Scopus |
| Efekt badań statutowych | NIE |
| Materiał konferencyjny: | NIE |
| Publikacja OA: | TAK |
| Licencja: | |
| Sposób udostępnienia: | Witryna wydawcy |
| Wersja tekstu: | Ostateczna wersja opublikowana |
| Czas opublikowania: | W momencie opublikowania |
| Data opublikowania w OA: | 16 września 2026 |
| Abstrakty: | angielski |
| This article examines the reuse of waste polyurethane foam (PUF) as a material in line with circular economy principles. The main objective was to evaluate how crushed polyurethane filler of different bulk densities—35 kg·m−3 (PUF35), 60 kg·m−3 (PUF60), and their blends at 1–5 wt%—affects the mechanical behaviour and structural integrity of hybrid composite systems and bonded laminated joints. An epoxy resin matrix was combined with 3D-printed polylactide (PLA) honeycomb structures, with rectangular and hexagonal core geometries. Static tensile tests showed that the blended filler (PUF35/60) preserves tensile strength and increases the modulus of elasticity for both core geometries, reaching maximum values at 4 wt% (3.8 GPa for rectangular, 3.6 GPa for hexagonal cores). In bonded lap joints, 1 wt% PUF35 resulted in the highest tensile adhesive bond strength (13.3 MPa). SEM confirmed a high-quality phase interface and continuous adhesive contact between the epoxy matrix and the 3D-printed PLA surface, with dominant cohesive failure and effective mechanical anchoring of foam particles, even near local printing defects. The results confirm mechanically recycled PUF as a promising filler for advanced sandwich structures and adhesive systems. |